Overview
NIIPPON VINILEX 130 ACTIVE PRIMER is a two-pack Polyvinyl butyral based, acid catalysed etching primer that is necessary to ensure good adhesion on all non-ferrous metals. Widely used by both manufacturing and heavy duty protection concerns. Environmental friendly product without containing Lead & Chrome Pigment as an anti-corrosive pigment.
Features:
- Quick dry for short recoating convenience
- High coverage requires only a thin coat. Economical to use
- Anti-corrosive property for short-term protection
- Excellent adhesion on all non-ferrous metals and blast cleaned steel
- Short term weather resistant
- Non Toxic and do not contain Heavy Metal such as Lead, Mercury, Cadmium, Chromium, Selenium, Antimony, Arsenic and Tar compound
Coating system
| Surface of metal; Non-Ferrous Metal | ||
| Type | Product | No. of coat |
| Sealer | Nippon Vinilex 130 Active Primer | 1 coat |
| Intermediate | Bilac Undercoat White | 1 coat |
| Finishing | Nippon Tilac | 1-2 coats |
Application data
 Application Methods |
Brush, roller, compressed airless spray and air spray |
 Mixing Ratio |
4 parts by volume of VINILEX 130 ACTIVE PRIMER BASE to 1 part by volume of VINILEX 130 ACTIVE PRIMER HARDENER. BASE and HARDENER to be mixed and stirred thoroughly for 20 minutes prior to application. Dilution should be done after the addition of hardener |
 Dilution |
Roller & Brush: 10% maximum Air Spray: 20% maximum Airless Spray: 5% maximum Thinner: Nippon Vinilex 125Thinner |
 Drying Time |
Dry to touch: 10 minutes Dry to handle: 1 hour |
 Overcoating Time |
2 hours. Minimum |
 Recommended Film Thickness |
15 microns for dry film 113 microns for wet film |
 Finish |
Sheen White |
 Packing |
5 Liters (4 Liters of BASE with 1 Liter of HARDENER) |